| A | B | C | D | E | F | G | H | I | J | K | L | M | N | O | P | Q | R | S | T | U | V | W | X | Y | Z | AA | AB | AC | AD | AE | AF | AG | AH | AI | AJ | ||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
1 | Strength and Stiffness | Density and Hardness | Toughness and Impact Resistance | Thermal Properties | Electrical Properties | Fatigue | Compression Recovery | ||||||||||||||||||||||||||||||
2 | Material | Cure Profile | Ultimate Tensile Strength (MPa) | Tensile Modulus (MPa) | Elongation at Break (%) | Stress @ 50% Elongation (MPa) | Stress @ 100% Elongation (MPa) | Shore Hardness | Printed Density (g/cc) | Gardner Impact Strength (1/16" thickness) (J) | Work of Fracture (J/m^2) | Notched Izod Impact Strength (J/m) | Heat Deflection Temperature @ 1.8 MPa (°C) | Heat Deflection Temperature @ 0.45 MPa (°C) | Thermal Conductivity (W/m*K) | Heat Capacity @ 25 °C (J/g*K) | Coefficient of Thermal Expansion (μm/m/°C) | Flammability (UL 94 Rating @ thickness tested) | Volume Resistivity | Surface Resistivity | Dielectric Constant (k') | Dielectric Strength (kV/mm) | Ross Flex Fatigue at 23 °C (30 deg 1Hz) (Cycles) | Compression Set (23 °C for 22 hours) | Compression Set (70 °C for 22 hours) | Surface Gloss | |||||||||||
3 | Clear Resin V5 | 5 min @ ambient temp, Form Cure V1 | 51 | 2575 | 10 | N/A | N/A | 78 D | 1.21 | < 0.2 | 26.7 | 29 | 54 | 61 | 0.54 | 1.8 | 114.1 | Not Tested | Not Tested | >1 x 10^12 | 4.28 @ 1 MHz | 16.3 | N/A | N/A | N/A | 89 (X/Y) 24 (Z) | |||||||||||
4 | Clear Resin V5 (Heated Cure) | 15 min @ 60C, Form Cure V1 | 60 | 2750 | 8 | N/A | N/A | 80 D | 1.21 | < 0.2 | 26.7 | 29 | 57 | 69 | 0.54 | 1.8 | Not Tested | Not Tested | Not Tested | >1 x 10^12 | 4.28 @ 1 MHz | 16.3 | N/A | N/A | N/A | 89 (X/Y) 24 (Z) | |||||||||||
5 | Black Resin V5 | 5 min @ ambient temp, Form Cure V1 | 57 | 2450 | 14 | N/A | N/A | 67 D | 1.21 | < 0.2 | 29.1 | 29 | 54 | 61 | 0.54 | 1.9 | 114.1 | Not Tested | Not Tested | >1 x 10^12 | 4.28 @ 1 MHz | 16.3 | N/A | N/A | N/A | 18 (X/Y) 2 (Z) | |||||||||||
6 | Black Resin V5 (Heated Cure) | 15 min @ 60C, Form Cure V1 | 61 | 2700 | 10 | N/A | N/A | 76 D | 1.21 | < 0.2 | 29.1 | 29 | 57 | 69 | 0.54 | 1.9 | Not Tested | Not Tested | Not Tested | >1 x 10^12 | 4.28 @ 1 MHz | 16.3 | N/A | N/A | N/A | 18 (X/Y) 2 (Z) | |||||||||||
7 | Grey Resin V5 | 5 min @ ambient temp, Form Cure V1 | 54 | 2500 | 15 | N/A | N/A | 80 D | 1.21 | < 0.2 | 28.6 | 34 | 54 | 62 | 0.54 | 1.8 | 114.1 | Not Tested | Not Tested | >1 x 10^12 | 4.28 @ 1 MHz | 16.3 | N/A | N/A | N/A | 32 (X/Y) 2 (Z) | |||||||||||
8 | Grey Resin V5 (Heated Cure) | 15 min @ 60C, Form Cure V1 | 62 | 2675 | 13 | N/A | N/A | 82 D | 1.21 | < 0.2 | 28.6 | 32 | 59 | 71 | 0.54 | 1.8 | Not Tested | Not Tested | Not Tested | >1 x 10^12 | 4.28 @ 1 MHz | 16.3 | N/A | N/A | N/A | 32 (X/Y) 2 (Z) | |||||||||||
9 | White Resin V5 | 5 min @ ambient temp, Form Cure V1 | 54 | 2500 | 15 | N/A | N/A | 73 D | 1.21 | < 0.2 | 35.2 | 29 | 54 | 62 | 0.54 | 1.5 | 114.1 | Not Tested | Not Tested | >1 x 10^12 | 4.28 @ 1 MHz | 16.3 | N/A | N/A | N/A | 35 (X/Y) 7 (Z) | |||||||||||
10 | White Resin V5 (Heated Cure) | 15 min @ 60C, Form Cure V1 | 62 | 2675 | 13 | N/A | N/A | 80 D | 1.21 | < 0.2 | 35.2 | 29 | 59 | 71 | 0.54 | 1.5 | Not Tested | Not Tested | Not Tested | >1 x 10^12 | 4.28 @ 1 MHz | 16.3 | N/A | N/A | N/A | 35 (X/Y) 7 (Z) | |||||||||||
11 | Fast Model Resin | 5 min @ ambient temp, Form Cure V1 | 55 | 2480 | 15 | N/A | N/A | 79 D | Not Tested | < 0.2 | 42.4 | 30 | 49 | 58 | Not Tested | 4.3 | Not Tested | Not Tested | Not Tested | >1 x 10^12 | Not Tested | Not Tested | N/A | N/A | N/A | 35 (X/Y) 7 (Z) | |||||||||||
12 | Fast Model Resin (Heated Cure) | 15 min @ 60C, Form Cure V1 | 62 | 2670 | 11 | N/A | N/A | Not Tested | Not Tested | < 0.2 | 42.4 | 37 | 61 | 76 | Not Tested | 4.3 | Not Tested | Not Tested | Not Tested | >1 x 10^12 | Not Tested | Not Tested | N/A | N/A | N/A | 35 (X/Y) 7 (Z) | |||||||||||
13 | Tough 1500 Resin V1 (Legacy) | 12 min @ 70 C, Form Cure V2 | 35 | 1440 | 54 | N/A | N/A | 76 D | 1.15 | 2.5 | 102 | 69 | 43 | 48 | Not Tested | Not Tested | 97 | Not Tested | Not Tested | Not Tested | 3.13 @ 6.78 MHz 3.07 @ 13.56 MHz 3.00 @ 27.12 MHz | Not Tested | N/A | N/A | N/A | Not Tested | |||||||||||
14 | Tough 1500 Resin V2 | 12 mins @ 70 C, Form Cure V2 | 34 | 1460 | 155 | N/A | N/A | 76 D | 1.12 | 11.1 | 1090 | 40 | 53 | 66 | 0.311 | 2.0 | HB @ 3mm | 3 x 10^15 | >1 x 10^12 | 4.5 @ 50 Hz 3.9 @ 1 kHz | 23.4 | 8000 | N/A | N/A | 25 (X/Y) 6 (Z) | ||||||||||||
15 | Tough 1000 Resin | 12 mins @ 70 C, Form Cure V2 | 26.3 | 932 | 180 | N/A | N/A | 68 D | 1.07 | 14.5 | 3200 | 72 | 44.6 | 55.3 | Not Tested | Not Tested | 168.2 | HB @ 3mm | 4 x 10^15 | Not Tested | 3.70 @ 50 Hz 3.59 @ 1 kHz | 15.1 | >100,000 | N/A | N/A | Not Tested | |||||||||||
16 | Tough 2000 Resin V1 (Legacy) | 7 mins @ 70C, Form Cure V2 | 46 | 2100 | 44 | N/A | N/A | 81 D | 1.2 | 2.1 | 115 | 41 | 50 | 59 | 0.270 | 2.0 | 91 | Not Tested | Not Tested | >1 x 10^12 | Not Tested | Not Tested | N/A | N/A | N/A | 22 (X/Y) 16 (Z) | |||||||||||
17 | Tough 2000 Resin V2 | 12 mins @ 70 C, cure v2 | 40.4 | 1800 | 79 | N/A | N/A | 76 D | 1.09 | 1.1 | 305 | 25 | 57 | 70 | Not Tested | Not Tested | 134.2 | HB @ 3mm | 3*10^15 | Not Tested | 3.46 @ 50 Hz 3.38 @ 1 kHz | 15.5 | 3560 | N/A | N/A | Not Tested | |||||||||||
18 | Durable Resin V2.1 (Legacy) | 60 mins @ 60C, cure v1 | 28 | 1000 | 55 | N/A | N/A | 70 D | 1.13 | 10.1 | 763 | 114 | Not Tested | < 30 | Not Tested | 2.1 | 106 | Not Tested | Not Tested | >1 x 10^12 | Not Tested | 31.1 | N/A | N/A | N/A | 65 (X/Y) 28 (Z) | |||||||||||
19 | Rigid 4000 Resin V1 | 15 mins @ 80C, cure v1 | 69 | 4100 | 5.3 | N/A | N/A | 84 D | 1.33 | < 0.2 | 63 | 23 | 60 | 77 | Not Tested | 1.9 | 63 | Not Tested | Not Tested | >1 x 10^12 | 3.22 @ 6.78 MHz 3.17 @ 13.56 MHz 3.07 @ 27.12 MHz | 29.5 | N/A | N/A | N/A | 5 (X/Y) 3 (Z) | |||||||||||
20 | Rigid 10K Resin V1 | 60 mins @ 70C, cure v1 | 65 | 10000 | 1 | N/A | N/A | 89 D | 1.7 | < 0.2 | 82.6 | 16 | 82 | 163 | 0.621 | 1.7 | 47 | HB @ 3mm | 1.1 x 10^15 | >1 x 10^12 | 2.72 @ 6.78 MHz 2.69 @ 13.56 MHz 2.65 @ 27.12 MHz 3.4 @ 1 GHz 3.3 @ 10 GHz | 18.0 | N/A | N/A | N/A | 4 (X/Y) 2 (Z) | |||||||||||
21 | Rigid 10K Resin V1 (Additional Thermal Cure) | 60 mins @ 70C, 125 min @ 90 C | 53 | 10000 | 1 | N/A | N/A | 89 D | 1.7 | < 0.2 | Not Tested | 18 | 110 | 218 | 0.621 | 1.7 | 46 | HB @ 3mm | 1.1 x 10^15 | >1 x 10^12 | 2.72 @ 6.78 MHz 2.69 @ 13.56 MHz 2.65 @ 27.12 MHz 3.4 @ 1 GHz 3.3 @ 10 GHz | 18.0 | N/A | N/A | N/A | 4 (X/Y) 2 (Z) | |||||||||||
22 | Flexible 80A Resin | 10 mins @ 60C, cure v1 | 8.9 | N/A | 120 | 3.1 | 6.3 | 80 A | 1.12 | N/A | N/A | N/A | N/A | N/A | Not Tested | Not Tested | Not Tested | Not Tested | Not Tested | >1 x 10^12 | 3.71 @ 6.78 MHz 3.60 @ 13.56 MHz 3.26 @ 27.12 MHz | Not Tested | >200,000 | 3% | 5% | Not Tested | |||||||||||
23 | Elastic 50A Resin V2 | 30 mins @ 70C, Form Cure V1 | 3.4 | N/A | 160 | 0.9 | 1.7 | 55 A | 1.01 | N/A | N/A | N/A | N/A | N/A | Not Tested | Not Tested | Not Tested | Not Tested | Not Tested | 2 x 10^10 | Not Tested | Not Tested | 800 | 2.10% | 3.10% | Not Tested | |||||||||||
24 | Silicone 40A Resin | 30 mins @ 60C, Form Cure V1 | 5 | N/A | 230 | 0.4 | 1 | 40 A | 1.02 | N/A | N/A | N/A | N/A | N/A | Not Tested | Not Tested | Not Tested | Not Tested | 2.3 x 10^14 | Not Tested | 2.9 | 17.4 | > 500,000 | 16% | Not Tested | Not Tested | |||||||||||
25 | High Temp Resin V2 | 60 mins @ 60C, Cure V1 | 58 | 2800 | 3.3 | N/A | N/A | 88 D | 1.19 | < 0.2 | 15.3 | 18 | 78 | 120 | Not Tested | 1.7 | 75 | Not Tested | Not Tested | >1 x 10^12 | 3.39 @ 6.78 MHz 3.33 @ 13.56 MHz 3.26 @ 27.12 MHz | Not Tested | N/A | N/A | N/A | 68 (X/Y direction) 46 (Z direction) | |||||||||||
26 | High Temp Resin V2 (Additional Thermal Cure) | 120 mins @ 80C, 180 mins @ 160C | 49 | 2800 | 2.3 | N/A | N/A | 1.19 | < 0.2 | Not Tested | 17 | 101 | 238 | Not Tested | 1.7 | 80 | Not Tested | Not Tested | >1 x 10^12 | 3.39 @ 6.78 MHz 3.33 @ 13.56 MHz 3.26 @ 27.12 MHz | Not Tested | N/A | N/A | N/A | |||||||||||||
27 | ESD Resin | 60 mins @ 70C | 44.2 | 1937 | 12 | N/A | N/A | 90 D | 1.116 | Not Tested | Not Tested | 26 | 54.2 | 62.2 | 0.305 | Not Tested | 68.7 | Not Tested | 10^5 - 10^7 | 10^5 - 10^8 | 26.95 @ 1 MHz | Not Tested | N/A | N/A | N/A | Not Tested | |||||||||||
28 | Flame Retardant Resin | 60 mins @ 70C | 38 | 2900 | 9.4 | N/A | N/A | 75 D | 1.25 | < 0.2 | 311 | 22.1 | 71 | 94 | Not Tested | Not Tested | 98.6 | V-0 @ 3mm V-1 @ 2.5mm HB @ 1.5mm | 2.1 x 10^15 | >1 x 10^12 | 3.83 @ 0.5 MHz 3.82 @ 1.0 MHz | 15.1 | N/A | N/A | N/A | 1 (X/Y direction) 0.8 (Z direction) | |||||||||||
29 | Flame Retardant Resin (Extended Cure) | 120 mins @ 80C | 41 | 3100 | 7.1 | N/A | N/A | 75 D | 1.25 | < 0.2 | 277 | 22.4 | 83 | 111 | Not Tested | Not Tested | 68.1 | V-0 @ 3mm V-1 @ 2.5mm HB @ 1.5mm | 2.1 x 10^15 | 3.83 @ 0.5 MHz 3.82 @ 1.0 MHz | 15.1 | N/A | N/A | N/A | |||||||||||||
30 | Alumina 4N Resin | Debound and sintered with the 2 furnace schedule found here | N/A | 370000 | N/A | N/A | N/A | N/A | 3.987 | N/A | N/A | N/A | N/A | N/A | 32 | Not Tested | 6 | N/A | 1 x 10^14 | Not Tested | 9.8 | Not Tested | N/A | N/A | N/A | N/A | |||||||||||
31 | Nylon 12 Powder | N/A | 50 | 1850 | 11 (X/Y) 6 (Z) | N/A | N/A | 74 D | 0.99 | 0.5 | Not Tested | 32 | 87 | 171 | 0.428 | Not Tested | 165 | HB @ 3mm | Not Tested | 1 × 10^11 | 2.86 @ 6.78 MHz 2.80 @ 13.56 MHz 2.74 @ 27.12 MHz | 8.82 | N/A | N/A | N/A | 1.2 (X/Y) 1.1 (Z) | |||||||||||
32 | Nylon 12 Tough Powder | N/A | 42 | 1450 | 25 (X/Y) 15 (Z) | N/A | N/A | 73 D | 1.01 | 0.6 | Not Tested | 60 | 46 | 161 | Not Tested | Not Tested | Not Tested | HB @ 3mm | Not Tested | 1 × 10^9 | 5.62 @ 1 MHz | 2.05 | N/A | N/A | N/A | Not Tested | |||||||||||
33 | Nylon 12 White Powder | N/A | 47 | 1950 | 8 (X/Y) 6 (Z) | N/A | N/A | Not Tested | Not Tested | Not Tested | Not Tested | 28 | 87 | 177 | Not Tested | Not Tested | Not Tested | HB @ 3mm | Not Tested | Not Tested | Not Tested | Not Tested | N/A | N/A | N/A | Not Tested | |||||||||||
34 | Nylon 12 GF Powder | N/A | 38 | 2800 | 4 (X/Y) 3 (Z) | N/A | N/A | 73 D | 1.33 | 0.7 (X/Y) 0.9 (Z) | Not Tested | 36 | 113 | 170 | 0.532 | Not Tested | 125.8 | HB @ 3mm | 1 × 10^12 | 3.19 @ 6.78 MHz 3.15 @ 13.56 MHz 3.10 @ 27.12 MHz | 8.54 | N/A | N/A | N/A | 1.5 | ||||||||||||
35 | Nylon 11 Powder | N/A | 49 | 1600 | 40 | N/A | N/A | Not Tested | Not Tested | Not Tested | Not Tested | 71 | 46 | 182 | Not Tested | Not Tested | Not Tested | Not Tested | Not Tested | Not Tested | 2.71 @ 6.78 MHz 3.15 @12.56 MHz 3.10 @ 27.12 MHz | Not Tested | N/A | N/A | N/A | Not Tested | |||||||||||
36 | Nylon 11 CF Powder | N/A | 69 (X) 52 (Y) 38 (Z) | 5300 (X) 2800 (Y) 1600 (Z) | 9 (X) 15 (Y) 5 (Z) | N/A | N/A | Not Tested | Not Tested | Not Tested | Not Tested | 74 | 178 | 188 | Not Tested | Not Tested | 47.2 | Not Tested | Not Tested | 1 × 10^3 | 31.7 @ 300 MHz 19 @ 1 GHz | Not Tested | N/A | N/A | N/A | Not Tested | |||||||||||
37 | TPU 90A Powder | N/A | 8.7 (X/Y) 7.2 (Z) | N/A | 310 (X/Y) 110 (Z) | 6.1 (X/Y) 5.9 (Z) | 7.2 (X/Y) 7 (Z) | 90 A | Not Tested | N/A | N/A | N/A | N/A | N/A | Not Tested | Not Tested | 235 | Not Tested | Not Tested | Not Tested | Not Tested | Not Tested | Not Tested | 20.50% | 59.90% | Not Tested | |||||||||||
38 | |||||||||||||||||||||||||||||||||||||
39 | |||||||||||||||||||||||||||||||||||||
40 | |||||||||||||||||||||||||||||||||||||
41 | |||||||||||||||||||||||||||||||||||||
42 | |||||||||||||||||||||||||||||||||||||
43 | |||||||||||||||||||||||||||||||||||||
44 | |||||||||||||||||||||||||||||||||||||
45 | |||||||||||||||||||||||||||||||||||||
46 | |||||||||||||||||||||||||||||||||||||
47 | |||||||||||||||||||||||||||||||||||||
48 | |||||||||||||||||||||||||||||||||||||
49 | |||||||||||||||||||||||||||||||||||||
50 | |||||||||||||||||||||||||||||||||||||
51 | |||||||||||||||||||||||||||||||||||||
52 | |||||||||||||||||||||||||||||||||||||
53 | |||||||||||||||||||||||||||||||||||||
54 | |||||||||||||||||||||||||||||||||||||
55 | |||||||||||||||||||||||||||||||||||||
56 | |||||||||||||||||||||||||||||||||||||
57 | |||||||||||||||||||||||||||||||||||||
58 | |||||||||||||||||||||||||||||||||||||
59 | |||||||||||||||||||||||||||||||||||||
60 | |||||||||||||||||||||||||||||||||||||
61 | |||||||||||||||||||||||||||||||||||||
62 | |||||||||||||||||||||||||||||||||||||
63 | |||||||||||||||||||||||||||||||||||||
64 | |||||||||||||||||||||||||||||||||||||
65 | |||||||||||||||||||||||||||||||||||||
66 | |||||||||||||||||||||||||||||||||||||
67 | |||||||||||||||||||||||||||||||||||||
68 | |||||||||||||||||||||||||||||||||||||
69 | |||||||||||||||||||||||||||||||||||||
70 | |||||||||||||||||||||||||||||||||||||
71 | |||||||||||||||||||||||||||||||||||||
72 | |||||||||||||||||||||||||||||||||||||
73 | |||||||||||||||||||||||||||||||||||||
74 | |||||||||||||||||||||||||||||||||||||
75 | |||||||||||||||||||||||||||||||||||||
76 | |||||||||||||||||||||||||||||||||||||
77 | |||||||||||||||||||||||||||||||||||||
78 | |||||||||||||||||||||||||||||||||||||
79 | |||||||||||||||||||||||||||||||||||||
80 | |||||||||||||||||||||||||||||||||||||
81 | |||||||||||||||||||||||||||||||||||||
82 | |||||||||||||||||||||||||||||||||||||
83 | |||||||||||||||||||||||||||||||||||||
84 | |||||||||||||||||||||||||||||||||||||
85 | |||||||||||||||||||||||||||||||||||||
86 | |||||||||||||||||||||||||||||||||||||
87 | |||||||||||||||||||||||||||||||||||||
88 | |||||||||||||||||||||||||||||||||||||
89 | |||||||||||||||||||||||||||||||||||||
90 | |||||||||||||||||||||||||||||||||||||
91 | |||||||||||||||||||||||||||||||||||||
92 | |||||||||||||||||||||||||||||||||||||
93 | |||||||||||||||||||||||||||||||||||||
94 | |||||||||||||||||||||||||||||||||||||
95 | |||||||||||||||||||||||||||||||||||||
96 | |||||||||||||||||||||||||||||||||||||
97 | |||||||||||||||||||||||||||||||||||||
98 | |||||||||||||||||||||||||||||||||||||
99 | |||||||||||||||||||||||||||||||||||||
100 | |||||||||||||||||||||||||||||||||||||